High Methoxyl Pectin–Tomato Paste Edible Films Formed Under Different Drying Temperatures

Pectin–tomato paste edible films with potential antioxidant activity were studied. Initially, the films were formed by drying at 40 °C in the presence and absence of glycerol. The effect of drying temperature on several physicochemical, mechanical, and optical properties of glycerol films formed after drying at 40, 50, and 60 °C was investigated. Finally, films formed at different drying conditions (namely F40, F50, and F60) sharing the same antioxidant activity (44.28–45.53%) were studied in terms of their surface pH; solubility; folding endurance; antimicrobial, dynamic mechanical, and barrier properties; contact angle; and FT-IR. Their thickness, weight, opacity, strength, stiffness, and antioxidant activity (AA) [a*] increased with increasing tomato paste content, whereas [L*] decreased. The moisture content was statistically affected by both the presence of glycerol and the drying temperature. AA decreased as drying temperature increased. Overall, the thickness varied from 45 to 182.31 μm, weight from 0.27 to 1.24 g, moisture content from 20.74 to 56.66%, stress from 189 to 959 kPa, Young’s modulus from 86 to 382 kPa, and AA from 16.9 to 53%. In the last step, F60 was less hydrophilic, had a greater density, and better barrier properties, whereas F50 was stiffer and the least strong. Our findings provide information regarding the selection of an optimum drying temperature for pectin-based films with antioxidant properties.