The Influence of Aging Temperature and Cryogenic Treatment on the Mechanical Properties and Microstructure of Extruded Mg-8Gd-3Y-0.4Zr Alloy

This investigation implemented an integrated aging-cryogenic thermal processing method for extruded Mg-8Gd-3Y-0.4Zr alloy to further improve its performance and broaden its scope of application, employing a characterization approach combining optical microscopy (OM), electron backscatter diffraction (EBSD), X-ray diffraction (XRD), and transmission electron microscopy (TEM). The comprehensive microstructure characterization was systematically correlated with mechanical property evolution to establish structure-property relationships. The results show that aging combined with cryogenic treatment significantly enhances the hardness and improves the microstructure of magnesium alloys. Specimens aged at 210 °C for 20 h followed by one-hour cryogenic treatment exhibited the highest average hardness (113.5 HV), representing a 11.2-25% improvement compared to those aged at lower temperatures. This enhancement can be attributed to the elevated aging temperature promoting substantial precipitation and subsequent growth of second phases such as Mg₃(Gd,Y), which benefit from sufficient thermal activation energy. The increased density and larger dimensions of these second phases contribute to enhanced hardness through elevated internal stress generation. However, their non-uniform distribution may induce localized stress concentration, consequently reducing hardness uniformity. Notably, specimens subjected solely to 210 °C aging for 20 h showed marginally lower hardness compared to their cryogenically treated counterparts, suggesting that although cryogenic treatment may refine grain structures and introduce dislocation defects to enhance hardness, its concurrent reduction in residual stresses might limit the overall improvement magnitude.