Poly(Methyl Methacrylate)-Based Core-Shell Electrospun Fibers: Structural and Morphological Analysis

Dicyclopentadiene (DCPD)–poly(methyl methacrylate) (PMMA) core–shell fibers were fabricated via coaxial electrospinning to develop a self-healing polymer composite. A PMMA shell containing a first-generation Grubbs catalyst was co-spun with a DCPD core at 0.5 mL h−1 and 28 kV, yielding smooth, cylindrical fibers. The diameter range of nanofibers was 300–900 nm, with 95% below 800 nm, as confirmed by FESEM image analysis. FTIR spectroscopy monitored shell integrity via the PMMA C=O stretch and core polymerization via the trans-C=C bands. The high presence of the 970 cm−1 band in the healed nanofiber mat and the minor appearance in the uncut core–shell mat demonstrated successful DCPD polymerization mostly where the intended damage was. The optical clarity of PMMA enabled the direct monitoring of healing progress via optical microscopy. The presented findings demonstrate that PMMA can retain a liquid active core and catalyst to form a polymer layer on a damaged site and could be used as a model material for other self-healing systems that require healing monitoring.