Investigation of Diffusion Induced Fiber–Matrix Interface Damages in Adhesively Bonded Polymer Composites

Composite materials have the advantages of high strength and low weight, and are therefore used in many areas. However, in humid and marine environments, mechanical properties may deteriorate due to moisture diffusion, especially in glass fiber reinforced polymers (GFRP) and carbon fiber reinforced polymers (CFRP). This study investigated the damage formation and changes in mechanical properties of single-layer adhesive-bonded GFRP and CFRP connections under the effect of sea water. In the experiment, 0/90 orientation, twill-woven GFRP (7 ply) and CFRP (8 ply) plates were produced as prepreg using the hand lay-up method in accordance with ASTM D5868-01 standard. CNC Router was used to cut 36 samples were cut from the plates produced for the experiments. The samples were kept in sea water taken from the Aegean Sea, at 3.3-3.7% salinity and 23.5 °C temperature, for 1, 2, 3, 6, and 15 months. Moisture absorption was monitored by periodic weighings; then, the connections were subjected to three-point bending tests according to the ASTM D790 standard. The damages were analyzed microscopically with SEM (ZEISS GEMINI SEM 560). As a result of 15 months of seawater storage, moisture absorption reached 4.83% in GFRP and 0.96% in CFRP. According to the three-point bending tests, the Young modulus of GFRP connections decreased by 25.23% compared to dry samples; this decrease was 11.13% in CFRP. Moisture diffusion and retention behavior were analyzed according to Fick's laws, and the moisture transfer mechanism of single-lap adhesively bonded composites under the effect of seawater was evaluated.