Effect of aging time on multiphase microstructure and high-temperature creep properties of weldable Ni3Al-based alloy with ultrafine β phase

Laser remelting provides a novel approach to refine multiphase strengthening structure in weldable Ni 3 Al-based alloy (particularly for β phase), significantly improving the creep property. However, the ultrafine multiphase strengthening structure evolution and creep performance in laser remelted alloy were still uncertain during heat treatment. In this paper, the evolution of ultrafine multiphase strengthening structure at 980 °C for 200–1100 h and high-temperature creep properties at 1000 °C/120 MPa in weldable Ni 3 Al-based alloy with ultrafine β were investigated. Meantime, the relationship between evolution of ultrafine multiphase strengthening structure and creep properties was revealed. The findings show that rapid transformation of near-spherical γ′ phase (laser remelted) into cubic γ′ phase (200 h), growth (500 h), R-type γ′ rafting structure (800 h) and coarsened (1100 h) in ultrafine γ′+γ dendrite of the alloy were promoted by 980 °C for 200–1100 h high-temperature aging treatment, which significantly reducing steady-state creep rate in different aged alloys. Meanwhile, the dissolution and growth of ultrafine β phase lead to size from 0.81 μm to 1.64–2.28 μm and volume fraction from 13.61 % to 5.03 %–4.07 %. This is accompanied by the improvement of morphology distribution, from long strip discontinuous network bad distribution to the near-spherical dispersion uniform distribution, which significantly improves accelerated creep stage life of alloy. Among them, the 1100 h aged alloy had the highest creep life of 137 h and lowest steady-state creep rate of 0.01086 %/h at 1000 °C/120 MPa. • Evolution of ultrafine multiphase structure was studied during high temperature aging. • The ultrafine β phase bad distribution was improved and refined size was maintained. • The evolution of primary, secondary and tertiary γ′ phases in the alloy was studied. • The relations between microstructure evolution and creep properties were revealed.

Authors

Institutions

Publication Details

Journal
Intermetallics
Published
2025-06-16
DOI
https://doi.org/10.1016/j.intermet.2025.108881
Citations
2
Primary Topic
Intermetallics and Advanced Alloy Properties
Type
article
Field-Weighted Citation Impact
1.43

Funders

Controls
|||
ALL TIME
JAN
FEB
MAR
APR
MAY
JUN
JUL
AUG
SEP
OCT
article

Effect of aging time on multiphase microstructure and high-temperature creep properties of weldable Ni3Al-based alloy with ultrafine β phase

Junting Luo, Peichang Zhang, Yatao Du, Jinlong Liu et al.
2 citations
Intermetallics
Intermetallics and Advanced Alloy Properties
1.43
article

Effect of aging time on multiphase microstructure and high-temperature creep properties of weldable Ni3Al-based alloy with ultrafine β phase

Junting Luo, Peichang Zhang, Yatao Du, Jinlong Liu, Weichao Wang, Chong Li, Jing Wu, Yongchang Liu, Shiyou Gao
article en
2 citations

Abstract

Laser remelting provides a novel approach to refine multiphase strengthening structure in weldable Ni 3 Al-based alloy (particularly for β phase), significantly improving the creep property. However, the ultrafine multiphase strengthening structure evolution and creep performance in laser remelted alloy were still uncertain during heat treatment. In this paper, the evolution of ultrafine multiphase strengthening structure at 980 °C for 200–1100 h and high-temperature creep properties at 1000 °C/120 MPa in weldable Ni 3 Al-based alloy with ultrafine β were investigated. Meantime, the relationship between evolution of ultrafine multiphase strengthening structure and creep properties was revealed. The findings show that rapid transformation of near-spherical γ′ phase (laser remelted) into cubic γ′ phase (200 h), growth (500 h), R-type γ′ rafting structure (800 h) and coarsened (1100 h) in ultrafine γ′+γ dendrite of the alloy were promoted by 980 °C for 200–1100 h high-temperature aging treatment, which significantly reducing steady-state creep rate in different aged alloys. Meanwhile, the dissolution and growth of ultrafine β phase lead to size from 0.81 μm to 1.64–2.28 μm and volume fraction from 13.61 % to 5.03 %–4.07 %. This is accompanied by the improvement of morphology distribution, from long strip discontinuous network bad distribution to the near-spherical dispersion uniform distribution, which significantly improves accelerated creep stage life of alloy. Among them, the 1100 h aged alloy had the highest creep life of 137 h and lowest steady-state creep rate of 0.01086 %/h at 1000 °C/120 MPa. • Evolution of ultrafine multiphase structure was studied during high temperature aging. • The ultrafine β phase bad distribution was improved and refined size was maintained. • The evolution of primary, secondary and tertiary γ′ phases in the alloy was studied. • The relations between microstructure evolution and creep properties were revealed.

IntermetallicsVol. 185
Tianjin University (CN), Yanshan University (CN)
National Natural Science Foundation of China, Natural Science Foundation of Hebei Province
Openalex Percentile: Top 19%
Intermetallics and Advanced Alloy Properties
1.43
AI Navigator

Ask Laika to Summarize, Analyze, and Connect papers live on the map.

Summarize Papers & Methodologies

Extract key findings, datasets, and comparative methods across publications.

Benchmark Rankings & Visual Analytics

Rank top research institutions, authors, funders, topics, and journals by Field-Weighted Citation Impact (FWCI) and paper volume with instant charts.

Connect Distant Disciplines

Bridge topological clusters on the map to find hidden collaborative intersections.