Effects of Pretreatment Processes on Grain Size and Wear Resistance of Laser-Induction Hybrid Phase Transformation Hardened Layer of 42CrMo Steel

To address the issue of surface grain coarsening in laser-induction hybrid phase transformation of 42CrMo steel, this study investigated the effects of four pretreatment processes (quenching-tempering (QT), laser-induction quenching (LIQ), laser-induction normalizing (LIN), and laser-induction annealing (LIA)) on the austenite grain size and wear resistance after laser-induction hybrid phase transformation. The results showed that QT resulted in a tempered sorbite structure, resulting in coarse austenite grains (139.8 μm) due to sparse nucleation sites. LIQ generated lath martensite, and its high dislocation density and large-angle grain boundaries led to even larger grains (145.5 μm). In contrast, LIN and LIA formed bainite and granular pearlite, respectively, which refined austenite grains (78.8 μm and 75.5 μm) through dense nucleation and grain boundary pinning. After laser-induction hybrid phase transformation, all specimens achieved hardened layer depths exceeding 6.9 mm. When the pretreatment was LIN or LIA, the specimens after laser-induction hybrid phase transformation exhibited surface microhardness values of 760.3 HV0.3 and 765.2 HV0.3, respectively, which were 12 to 15% higher than those of the QT- and LIQ-pretreated specimens, primarily due to fine-grain strengthening. The friction coefficient decreased from 0.52 in specimens pretreated by QT and LIQ to 0.45 in those pretreated by LIN and LIA, representing a reduction of approximately 20%. The results confirm that regulating the initial microstructure via pretreatment effectively inhibits austenite grain coarsening, thereby enhancing the microhardness and wear resistance after transformation.