One-Step Hydrothermal Synthesis of Multicolour Graphene Quantum Dots and Study of Their Luminescence Mechanism

Multicolour graphene quantum dots (GQDs), from blue to orange emitting, were successfully synthesized via a one-step hydrothermal method using potassium hydrogen phthalate and o-phenylenediamine as the raw materials. After purification by silica gel column chromatography, four kinds of GQDs with maximum emission wavelengths of 420 nm (blue), 500 nm (green), 540 nm (yellow), and 555 nm (orange) were obtained, and all had a high quantum yield (9.7%, 8.8%, 9.3%, and 10.3%, respectively). The structural characterization revealed that the synthesized GQDs had a regular morphology, with a size of 2–3 nm and a thickness of 1–2 nm. The D-band-to-G-band ratio was less than 0.3, indicating that the GQDs had a high degree of graphitization. In addition, the emission peaks of the GQDs were red-shifted as the particle size increased, confirming that their luminescence was dominated by the quantum confinement effect. By analyzing the surface states and the functional groups of the multicolour GQDs, it was found that the GQDs had a similar elemental composition, which further proved that the emission wavelengths did not depend on the surface element composition, but conformed to the luminescence mechanism regulated by the quantum-limited effect. Furthermore, the four types of GQDs exhibited low cytotoxicity and good stability, suggesting their potential applications in biomarkers and for the synchronous detection of a variety of analytes.