MXenes as a Tool to Control p-Type Conductivity in ZnO Thin Film

This study demonstrates the selective tuning of p-type and n-type conductivity in ZnO thin films by incorporating MXenes at varying molar concentrations. ZnO thin films were fabricated using a cost-effective sol-gel method and annealed at 4500C under thermal and magnetically assisted conditions. Rietveld analysis of the hot point probe and Hall measurements were performed to confirm the conductivity variations induced by MXene doping. The results suggest that the conductivity of n-ZnO increased significantly from 0.27 mho/cm to 1274 mho/cm, while p-ZnO conductivity ranged from 0.0012 mho/cm to 6.2 × 10-4 mho/cm and 3.3 × 10-3 mho/cm to 0.84 mho/cm under magnetic fields of 280 G and 400 G, respectively. XRD analysis revealed a polycrystalline structure with an average grain size of about 100 nm. This novel approach offers a versatile method to control ZnO thin-film conductivity, including an extensive analysis of magnetic properties.