Influence of Different Surface Treatments on the Low-Temperature Degradation of Three Commercial Yttria-Stabilized Tetragonal Zirconia Polycrystal
Aging of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) under wet conditions is known as low-temperature degradation (LTD), which is associated with phase change and decreasing mechanical strength. Herein, we studied the effects of different surface treatments on the LTD of three different commercial Y-TZP blocks utilizing CAD/CAM technology, namely, <b>Cercon<sup>®</sup>, e.max<sup>®</sup> ZirCAD</b>, and <b>Vita In-ceram<sup>®</sup> YZ</b>. The blocks were immersed in 4% acetic acid at 80 °C for 0, 7, 14, and 28 days. The effects of surface treatments such as sandblasting and polishing were also examined. The results showed that the monoclinic phase increased with immersion time in all three brands. In <b>Cercon<sup>®</sup></b> blocks, a minimal amount of phase transformation was observed, with the smallest amount of degradation after immersion. Sandblasting and polishing both suppressed phase transformation. After immersion, the mechanical strength exhibited a small decrease with time. Accelerating the evaluation of the LTD of zirconia may effectively help with clinical applications.
Authors
- Wen-Fu Ho (ORCID: https://orcid.org/0000-0003-2355-7939)
- Hsueh-Chuan Hsu (ORCID: https://orcid.org/0000-0002-2643-1680)
- Shih-Ching Wu (ORCID: https://orcid.org/0000-0002-2042-8325)
- Jumei Tian (ORCID: https://orcid.org/0000-0003-3411-6186)
- Hongxin Liao (ORCID: https://orcid.org/0000-0002-3264-2601)
Institutions
- National Chiayi University (TW)
- National University of Kaohsiung (TW)
- Central Taiwan University of Science and Technology (TW)
Publication Details
- Journal
- Materials
- Published
- 2025-05-28
- DOI
- https://doi.org/10.3390/ma18112543
- Primary Topic
- Advanced ceramic materials synthesis
- Type
- article
- Field-Weighted Citation Impact
- 0.00