Effect of Print Orientation and Thermal Aging on the Flexural Strength of Zirconia-Reinforced Three-Dimensional-Printed Restorative Resin Materials

This study evaluated the effects of print orientation and thermal aging on the flexural strength (FS) and flexural modulus (FM) of novel permanent three-dimensional (3D)-printed polymethyl methacrylate (PMMA) resins reinforced with nano-zirconia and nano-silica. Bar-shaped specimens (25 × 2 × 2 mm) were fabricated using a digital light processing (DLP) 3D printer (Asiga Max UV, Asiga Inc., Australia) in two orientations (0° and 90°). Specimens underwent three-point bending tests at 24 h and after artificial thermal aging (10,000 and 30,000 cycles) to simulate one and three years of intraoral conditions. Scanning electron microscopy (SEM) was used to analyze fracture patterns. Print orientation did not significantly affect FS or FM (<i>p</i> > 0.05). However, artificial aging significantly reduced FS and FM after 10,000 cycles (<i>p</i> < 0.001), with further deterioration after 30,000 cycles. The micro hybrid resin composite exhibited higher FS than the 3D-printed materials throughout aging. SEM analysis revealed distinct fracture patterns, with 3D-printed resins displaying radial fractures and the micro hybrid composite exhibiting horizontal fractures. These findings indicate that aging plays a more critical role in the long-term mechanical performance of 3D-printed restorative resins than print orientation. This study provides original data on the effects of print orientation and prolonged thermal aging on the mechanical behavior of permanent three-dimensional (3D)-printed dental resins. Furthermore, the comparative evaluation of aging protocols simulating one and three years of intraoral service represents a novel contribution to the existing literature. Further studies are required to optimize the mechanical durability of 3D-printed dental restorations.