Interfacial Modulation of Laser-Deposited Ti6Al4V-TiC Wear-Resistant Coatings: Surface Ni-P Metallization of TiC Particles

Prior to the laser processing, the surface of the TiC-reinforced particles underwent a metallization process with Ni-P, with the objective of enhancing the wettability between the TiC and the Ti6Al4V, thereby ensuring enhanced wear resistance of the titanium-based composite (TMC) coatings. In this study, the chemical deposition method was utilized to synthesize three types of metallized TiC with varying phosphorus contents. The P contents of these samples were determined to be 9.12 wt.% (HP metallized TiC), 6.55 wt.% (MP metallized TiC), and 1.71 wt.% (LP metallized TiC). It was observed that the thickness of the coatings increased in a gradual manner with the decrease in P. Furthermore, the coating of the LP metallized TiC was found to possess the highest degree of crystallinity and a microcrystalline structure. The 50 wt.% TiC-Ti6Al4V composite coatings (TMC-Nickel-free, TMC-HP, TMC-MP, and TMC-LP) were produced by laser fusion deposition using untreated TiC and three metallized TiC enhancements. The findings indicate that TMC-LP exhibits cracking only during the initial processing stage. Surface metallization has been shown to enhance the wear resistance of composite coatings through several mechanisms, including increased bonding of the ceramic phase to the metal matrix and the formation of hard Ti2Ni compounds. The wear rates of TMC-HP, TMC-MP, and TMC-LP were reduced by 22%, 43%, and 72%, respectively, in comparison to TMC-Nickel-free.