Electrosynthesis and Phase Control of Cobalt-Based Nanoparticles: Antibacterial and Antifungal Evaluation of Co3O4 Formed at Varied Temperatures

This work successfully prepared the Co3O4 NPs via simple galvanostatic deposition followed by annealing at 400 and 800 °C for two hours. The galvanostatic deposition was carried out from a modified Watts bath. We used Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), energy dispersive X-ray (EDX), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) to examine the oxide’s characterization properties. The nature of the oxide formed was strongly dependent on the annealing temperature. The powder formed at room temperature (25 °C) is a mixture of Co(OH)2 and metallic Co. However, at 400 and 800 °C, and according to the XRD patterns, the powder consists of the Co3O4 phase and a slight quantity of Co(OH)2 phase. The average particle size measured by TEM ranged from 14.85 nm at room temperature to 90.19 nm at 800 °C. Moreover, the study examined how the operating deposition parameters affected the galvanostatic deposition process. Furthermore, these baths provide NPs, that demonstrate antibacterial activity against both Gram-positive (Staphylococcus aureus) and Gram-negative (Escherichia coli) bacteria as well as antifungal activity against Aspergillus niger.