Effective Treatment of High Arsenic Smelting Wastewater Synergetic Synthesis of Well-Crystallized Scorodite

Arsenic-containing acidic wastewater from nonferrous heavy smelting industry is a dangerous source of arsenic pollution due to its complex composition, high acidity, and strong toxicity. In this study, an environment-friendly strategy was proposed, in which highly stable scorodite was synthesized in acidic wastewater. The effects of initial pH, Fe/As molar ratio, and oxidation-reduction potential (ORP) on the morphology, particle size, phase composition, and leaching stability of scorodite were systematically investigated. The results demonstrate a distinct morphological evolution with increasing pH. The products were transitioned from bone-shaped to rice grain-shaped, and then turned to bipyramidal polyhedral-shaped and amorphous aggregates. When the Fe/As molar ratio was increased, the scorodite crystallization quickly formed well-defined particles (the size was 15–20 μm). Higher ORP values led to progressively irregular morphologies, reduced particle sizes, and ultimately formed amorphous ferric arsenate. The large-grained scorodite with regular morphology and high leaching stability from high-arsenic solutions (25 g/L) was produced under optimal conditions (initial pH 1.5, Fe/As 1.5, ORP 385 mV). These findings provide critical technical support for arsenic solidification from waste liquids under atmospheric pressure conditions.