Synthesis and Photoluminescent Properties of Dy3+-Doped and Dy3+/Eu3+ Co-Doped 50ZnO:40B2O3:5WO3:Nb2O5 Glass

Dy³⁺ single-doped and Dy³⁺/Eu³⁺ co-doped ZnO:B₂O₃:WO₃:Nb₂O₅ glass was successfully synthesized using the melt quenching method. The amorphous character of the prepared samples was confirmed by X-ray diffraction (XRD). The glass transition and crystallization temperatures were examined by differential scanning calorimetry (DSC). Raman spectroscopy was applied to investigate the glass microstructure. Physical properties like the density, molar volume, oxygen molar volume and oxygen packing density of the glass were also determined. The photoluminescence excitation (PLE) and emission (PL) spectra of the resultant glass types were measured. The obtained Dy³⁺ single-doped glass was characterized by strong luminescence at 482 and 574 nm, corresponding to the ⁴F_9/2 → ⁶H_15/2 (blue) and ⁴F_9/2 → ⁶H_13/2 (yellow) transitions, respectively, and weak luminescence at 663 nm and 753 nm due to the ⁴F_9/2 → ⁶H_11/2 (red) and ⁴F_9/2 → ⁶H_9/2 + ⁶F_11/2 (red) transitions. The luminescence results indicate that energy transfer from the Dy³⁺ to Eu³⁺ ions occurs in the proposed glass system. The emitted light from the Dy³⁺ single-doped glass was found to be yellow-orange. The Dy³⁺/Eu³⁺ co-doped samples emitted darker orange light. The obtained results show that the investigated types of glass have the potential to be used as orange light-emitting materials.