Integrating Backscattered Electron Imaging and Multi-Feature-Weighted Clustering for Quantification of Hydrated C3S Microstructure

The microstructure of cement paste is governed by the hydration of its major component, tricalcium silicate (C3S). Quantitative analysis of C3S microstructural images is critical for elucidating the microstructure-property correlation in cementitious systems. Existing image segmentation methods rely on image contrast, leading to a struggle with multi-phase segmentation in regions with close grayscale intensities. Therefore, this study proposes a weighted K-means clustering method that integrates intensity gradients, texture variations, and spatial coordinates for the quantitative analysis of hydrated C3S microstructure. The results indicate the following: (1) The deep convolutional neural network with guided filtering demonstrates superior performance (mean squared error: 53.52; peak signal-to-noise ratio: 26.35 dB; structural similarity index: 0.8187), enabling high-fidelity preservation of cementitious phases. In contrast, wavelet denoising is effective for pore network analysis but results in partial loss of solid phase information. (2) Unhydrated C3S reflects optimal boundary clarity at intermediate image relative resolutions (0.25–0.56), while calcium hydroxide peaks at 0.19. (3) Silhouette coefficients (0.70–0.84) validate the robustness of weighted K-means clustering, and the Clark–Evans index (0.426) indicates CH aggregation around hydration centers, contrasting with the random CH distribution observed in Portland cement systems.