Effect of Calcium Chloride on the Reinforcement of Uranium Tailings with Sodium Hydroxide–Sodium Silicate–Metakaolin

The uranium tailings mineral body is large and loose, and this could lead to radioactive contamination. Nuclides and heavy metals released from uranium tailings can be reduced through reinforcement treatment. The current study investigated the effect of CaCl2 solutions with the same volume and different mass fractions on uranium tailing reinforcement under the premise of fixing the dosage of metakaolin, sodium hydroxide, sodium silicate, and the water reducer. It was found that, when 20.0% CaCl2 was injected, the hydration reaction occurred more efficiently, and a more uniform gel polymer was produced. The degree of polymerization was higher, as well as the degree of aggregation near macropores. A large number of closed mesopores formed on the solidified surface. The pore structure of the solidified body was significantly improved; uranium ore particles had smaller gaps between them; the solidified body was better compacted; the leaching rates of uranium and its heavy metal ions were significantly reduced; and the compressive strength of the solidified body improved. In the triaxial test, the solidified body had a strength increase of 4.7 times. In addition to SEM, XPS, and XRD, the solidified samples were analyzed. In uranium slag solidified bodies, C-S-H and C-A-H gels and C-A-S-H and N-A-S-H polymers were formed. The gel polymers were wrapped around the uranium tailing particles, resulting in an 82.6% reduction in uranium leaching and a 57.2% reduction in radon exhalation.