The Effect of Austempering Temperature on the Matrix Morphology and Thermal Shock Resistance of Compacted Graphite Cast Iron

The significance of the matrix morphology of vermicular cast iron for the alloy's thermal shock resistance was determined. The study included vermicular cast iron subjected to heat treatment in order to obtain an ausferritic matrix. Heat treatment involved austenitization at 960 °C for 90 min, followed by two different austempering variants at 290 °C and 390 °C, each for 90 min. Austempering at 390 °C resulted in a higher content of retained austenite compared to austempering at 290 °C. A test stand was used to determine thermal shock resistance, enabling repeated heating and cooling of the samples. The samples were heated inductively and subsequently cooled in water at a constant temperature of approximately 30 °C. The total length of cracks formed on the wedge-shaped surfaces of the tested samples was adopted as a characteristic value inversely proportional to the material's thermal shock resistance. The samples heated to 500 °C were subjected to 2000 heating-cooling test cycles. It was found that in as-cast iron, structural changes were minor, whereas in the heat-treated material, changes in the structure were more noticeable. Under the influence of thermal shocks, ausferrite transforms into ferrite with carbides. Among the analyzed materials, the most resistant cast iron was the one austempered at 290 °C. Oxide precipitates were observed near cracks and graphite regions.