New (Co)poly(hydroxyimide)s Based on 4,4′-Oxydiphthalic Anhydride—Effect of Composition on Properties, Including Gas Transport Ability

This paper presents novel soluble (co)poly(hydroxyimide)s ((co)PIOH) based on 4,4'-oxydiphthalic anhydride (ODPA), 3,3'-dihydroxybenzidine (HAB), and 3,6-diaminodurene (D) with the 3/1, 1/1, and 1/3 HAB/D ratios. This chemical structure of the compounds provides the possibility of their future modification through the thermal rearrangement (polybenzoxazoles) or functionalization via Mitsunobu reaction (azo side-chain polyimides), i.e., obtaining new materials with interesting properties and therefore with expanded applications. Copolymers were characterized via FTIR, NMR, XRD, and GPC methods to confirm their structure, composition, and molar masses. The effect of copolymer composition on the thermal, mechanical, optical, and permeation properties studied for He, O₂, N₂, and CO₂, as well as hydrophobicity, was investigated. They exhibited a large interval between the glass transition temperature and the decomposition temperature, making them promising for the thermoforming technique. Transmittance above 90% was noted in the visible range for all (co)PIOH films deposited on a glass substrate. Young's modulus of fabricated membranes was in the range of 2.37 to 3.38 GPa. The highest permeability coefficients were recorded for (co)PIOH with a 1:3 HAB-to D-ratio.