Impact of Alkali-Activated Tannery Sludge-Derived Geopolymer Gel on Cement Properties: Workability, Hydration Process, and Compressive Strength

The utilization of tannery sludge (TS) in construction materials not only effectively reduces pollution and resource consumption associated with waste disposal, but also promotes low carbon transformation in the building materials sector, further advancing sustainable development of green construction. This study aims to investigate the impact of sludge-based geopolymer gel on cementitious material performance, revealing the evolution mechanisms of material fluidity, setting time, hydration process, and compressive strength under the coupled effects of tannery sludge and alkali activation, thereby providing a reusable technical pathway to address the resource utilization challenges of similar special solid wastes. A series of alkali-activated composite cementitious materials (AACC) were prepared in the study by partially substituting cement with alkaline activators, TS, and fly ash (FA), through adjustments in TS-FA ratios and alkali equivalent (AE) variations. The workability, hydration process, and compressive strength evolution of AACC were systematically investigated. The experimental results indicated that as the TS content increased from 0% to 100%, the fluidity of fresh AACC decreased from 147 mm to 87 mm, while the initial and final setting times exhibited an exponential upward trend. The incorporation of TS was found to inhibit cement hydration, though this adverse effect could be mitigated by alkaline activation. Notably, 20-40% sludge dosages (SD) enhanced early-age compressive strength. Specifically, the compressive strength of the 0% TS group at 3 d age was 24.3 MPa, that of the 20% TS group was 25.9 MPa (an increase rate of 6.58%), and that of the 40% TS group was 24.5 MPa (an increase rate of 0.82%), whereas excessive additions resulted in the reduction of hydration products content and diminished later stage strength development. Furthermore, the investigation into AE effects revealed that maximum compressive strength (37.4 MPa) was achieved at 9% AE. These findings provide critical data support for realizing effective utilization of industrial solid wastes.