Development of Chitosan-Coated Tung Oil Microcapsules with Antioxidants from Bamboo Leaves for Enhanced Antimicrobial Waterborne Coatings

Antibacterial microcapsules were prepared by using a compound of chitosan with an antioxidant of bamboo leaves (AOB) as the wall material and tung oil as the core material. The microcapsules were modified by adding them to waterborne coatings, and the modified waterborne coatings were coated onto Basswood samples. The performance of the obtained coatings was then characterised through a comparative analysis. The investigation focused on the effect of varying percentages of chitosan and AOB in microcapsules with a constant core-to-wall ratio on the performance of the waterborne on the surface of Basswood. The core-to-wall ratio of the microcapsules was established at 1:2, with the ratios of chitosan and AOB in the walls fixed at 9:1, 8:2, and 7:3, respectively. The results demonstrated that the gloss, impact resistance, and hardness of the coatings exhibited an increase with increasing ratios of AOB under varying Mchitosan:MAOB (MC:MA) conditions. Conversely, the adhesion exhibited a decrease with an increase in AOB. The colour difference value exhibited minimal change. The self-healing rate of the coating exhibited an initial increase, followed by a subsequent decrease, in response to the increasing AOB concentration. The antimicrobial effect was optimised at a ratio of 9:1 for the combination of chitosan and AOB. The coating of Basswood containing 1.0% microcapsules and 9:1 MC:MA demonstrated superior performance, exhibiting a gloss of 9.7 GU, a colour difference ΔE of 31.03, a hardness of HB, an adhesion rating of grade 1, an impact resistance of grade 4, a self-healing rate of 19.09%, and a noteworthy antimicrobial effect against both Escherichia coli and Staphylococcus aureus.