The Effect of Pulse Frequency on the Microstructure and Corrosion Resistance of an AZ31B Magnesium Alloy Composite Coating with Electron-Beam Remelting and Micro-Arc Oxidation

This study presents a systematic investigation into the influence of pulse frequency on the micro-arc oxidation (MAO) coating of AZ31B magnesium alloy following electron-beam remelting (EBR). The morphology, thickness, and corrosion resistance of the EBR-MAO composite coating were meticulously analyzed across various pulse frequencies (100 Hz, 200 Hz, 300 Hz, 400 Hz) employing scanning electron microscopy (SEM), X-ray diffraction (XRD), and electrochemical measurement techniques. The results show that as the pulse frequency escalates from 100 Hz to 400 Hz, the average thickness of the EBR-MAO composite coating diminishes from 41.1 μm to 38.5 μm, reduced by 6.7% compared to 10.4% in the MAO coating. Concurrently, the porosity exhibits a reduction from 1.93% to 1.35%, accompanied by a densification of the coating's structure. High pulse frequencies yield coatings with enhanced smoothness and fewer defects. Notably, the corrosion resistance of the coatings demonstrates significant improvement at higher frequencies (400 Hz) compared to their lower-frequency (100 Hz) counterparts, as evidenced by a tenfold increase in corrosion current density. This research underscores the pivotal role of pulse frequency in optimizing the protective qualities of MAO coatings on magnesium alloys.