High-Temperature Layered Modification of Mn2In2Se5

Layered chalcogenides are interesting from the point of view of the formation of two-dimensional magnetic systems for relevant applications in spintronics. High-spin Mn²⁺ or Fe³⁺ cations with five unpaired electrons are promising in the search for compounds with interesting magnetic properties. In this study, a new layered modification of the Mn₂In₂Se₅ compound from the A₂B₂X₅ family ("225") was synthesized and investigated. A phase transition to the polymorph with primitive trigonal lattice was recorded at a temperature of 711 °C, which was confirmed by simultaneous thermal analysis, X-ray powder diffraction at elevated temperatures, and sample annealing and quenching. The stability of Mn₂In₂Se₅ in air at high temperatures was investigated by thermal gravimetric analysis and powder X-ray diffraction. The new polymorph of Mn₂In₂Se₅ crystallizes in the Mg₂Al₂Se₅ structure type, as revealed by the Rietveld refinement against powder X-ray diffraction data. The crystal structure can be viewed as a close-packing of Se anions, in which indium and manganese cations are enclosed inside tetrahedral and octahedral voids, respectively, according to the <i>A</i>_Mn<i>B</i>_In<i>CB</i>_In<i>C</i>_Mn<i>A</i>… sequence. Magnetization measurements reveal an antiferromagnetic-like transition at a temperature of 6.3 K. The same magnetic properties are reported in the literature for the low-temperature R-centered trigonal polymorph. An approximation by the modified Curie-Weiss law yields a significant ratio of |<i>θ</i>|/<i>T</i>_N = 28, which indicates strong magnetic frustration.