Synergistic Effects of Thermal Cycles and Residual Stress on Microstructural Evolution and Mechanical Properties in Monel 400 and AISI 316L Weld Joints

The current study investigates the thermal, metallurgical, and mechanical results in similar and dissimilar weldments of Monel 400 and AISI 316L. Infrared thermography (IRT) was employed to record thermal cycles, while X-ray diffraction (XRD) was used to analyze the residual stresses post-welding. Mechanical properties were assessed through tensile and microhardness tests, and microstructural evolution was examined using energy-dispersive spectroscopy (EDS) and scanning electron microscopy (SEM). IRT results showed peak temperatures of 1788 °C for Monel 400 and 1750 °C for AISI 316L. Residual stress analysis revealed compressive stresses of 293 MPa in dissimilar welds, compared to 235 MPa in Monel 400 and tensile stresses of 57 MPa in AISI 316L. Ultimate tensile strength (UTS) values were 543 MPa for dissimilar welds, 533 MPa for Monel 400, and 556 MPa for AISI 316L, with corresponding microhardness values of 207 HV, 203 HV, and 168 HV, respectively. Microstructural analysis identified coarse Ni-Cu phases in the Monel 400 heat-affected zone (HAZ), austenitic structures in AISI 316L, and intermetallic compounds in dissimilar welds. The findings highlight the impact of thermal distribution, residual stress, and microstructural evolution on weld performance, providing insights into optimized welding parameters for improved joint integrity and mechanical properties.