Electron Beam Surface Treatment and Its Impact on the Plasticity of Fe-Based High-Entropy Alloy

In this work, we present results on the impact of electron beam surface modification on the phase composition, microstructure, chemical composition, and mechanical properties of Fe-Ni-Cr-Mo-W high-entropy alloy. During the experiments, the beam power was 600 and 1200 W. The phase composition was studied using XRD measurements. Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) were used to analyze the microstructure and chemical composition, respectively. The results showed that at the lower value of the power of the electron beam, a distinguished modified zone cannot be observed. With an increase in the discussed technological parameter, a treated zone with a thickness of about 30 μm can be seen on the top of the sample. The modulus of elasticity on the surface of the unprocessed alloy was measured to be 130 GPa and increased to 156 GPa in the case of both technological regimes of the electron beam surface modification process. The hardness on the top of the untreated alloy was about 4.5 GPa and reduced to about 3 GPa in the case of electron beam treatment on the alloy with a beam power of 600 W. The application of the modification process with a higher value of beam power, 1200 W, led to an even further decrease in the hardness, to about 2.8 GPa. The resistance to plastic deformation of the surface of the considered specimens was also analyzed via the H3/E2 ratio, and the results show that the application of the treatment procedure leads to a decrease in the resistance to plastic deformation in both cases. This decrease is more pronounced in the case of the treatment with the higher value of power of the electron beam.