Experimental Study on the Mechanical Properties of Cracked Limestone Reinforced by Modified Cement Grouting

Grouting reinforcement is a pivotal approach to enhancing the integrity and load-bearing capacity of fractures in surrounding rock. In this study, standard limestone specimens were fractured through uniaxial compression. Then, the specimens were reinforced with grouting, using ultrafine cement paste containing varying mass fractions of enhancers and a grouting apparatus developed by the authors. After the specimens were cured under standard conditions for 28 days, CT scanning technology was used to investigate the microstructure and grouting effect characteristics of grouted bodies containing different mass fractions of enhancers from a mesoscopic perspective. Then, uniaxial compression tests were conducted on those grouted specimens. The experimental results revealed that the content of the enhancer significantly affected the post-peak characteristics, mechanical parameters, and failure modes of the grouted specimens. When the content of the enhancer increased from 2.50 wt.% to 15.00 wt.%, the uniaxial compressive strength of the grouted specimens exhibited a positive correlation with the enhancer content, with the maximum improvement rate reaching 18.10% compared to the residual strength. However, when the enhancer content ranged from 15.00 wt.% to 20.00 wt.%, the uniaxial compressive strength was negatively correlated with the enhancer content. At an enhancer content of 15.00 wt.%, the overall stability of the grouted specimens was optimal, with all mechanical parameters reaching their maximum values. Utilizing three-dimensional CT scanning and reconstruction technology, it was observed that when the enhancer content was less than 15.00 wt.%, the cracks were concentrated in the limestone matrix rather than in the grouted solid in the edge regions of grouted specimens. However, in the whole specimens, the cracks in the grouted solid exceeded that in the limestone matrix. Conversely, when the enhancer content was greater than 17.50 wt.%, the grouted solid was predominantly distributed within the edge fissures of the specimens, while the internal regions exhibited a lower volume fraction of the grouted solid. In this scenario, the volume fraction of the grouted solid in the specimens was significantly lower than that of the fissures.