Investigation of the Flexural and Tensile Properties of Hybrid Polyester Composites Reinforced with Bamboo Fibers and Red Mud Waste

This article discusses research on utilizing natural fibers and red mud waste as eco-friendly alternatives in the production of polymer matrix composites. In this study, composites of isophthalic unsaturated polyester matrix were produced by combining bamboo fibers (<i>Bambusa vulgaris</i>) and red mud waste. The red mud waste utilized had a particle size of 50-100 mesh, and the fibers measured 15 mm and 30 mm in length, distributed randomly throughout the matrix. Bamboo fibers were utilized in their raw form and underwent treatment with NaOH (5% for 2 h). The composites underwent mechanical assessment via flexural and tensile testing. The mechanical properties measured were analyzed using analysis of variance (ANOVA) and Tukey's test. The fracture surfaces of the composites were examined using Scanning Electron Microscopy (SEM). Composites featuring 30 mm long treated fibers and 30% red mud exhibited improved flexural strength (124.71 MPa), along with a deformation of 2.16 mm and a flexural modulus of 15.79 GPa. Tensile tests revealed that incorporating red mud waste significantly enhanced the tensile strength by 68% (15BTRMW10) compared to neat polyester. ANOVA confirmed the dependability of the findings, emphasizing the viability of producing hybrid composites from red mud waste and bamboo fiber.