Phase Transformation and Deformation Mechanisms of 304L Stainless Steel Under Tensile and Charpy Impact Testing at Varying Temperatures

This study examines the mechanical behavior and deformation mechanisms of hot-forged 304L stainless steel for cryogenic applications such as LNG storage and low-temperature structural systems. Tensile testing revealed a significant strength increase from 618 MPa at room temperature to 1432 MPa at cryogenic temperatures, with elongation decreasing from 83.7% to 23.3%. Charpy impact testing showed a 28% reduction in absorbed energy at cryogenic temperatures due to enhanced strain-induced martensitic transformation (SIMT). The observed mechanical responses are attributed to reduced stacking fault energy (SFE) at lower temperatures, which promotes SIMT, deformation twinning, and dislocation interactions, affecting material strength and toughness. SEM and EBSD analysis confirmed extensive martensitic transformation, increased deformation twinning, and reduced remaining austenite, indicating a γ → ε → α’ transformation pathway that governs strain hardening. The high strain rate during Charpy impact testing induced localized adiabatic heating, partially suppressing SIMT and modifying fracture behavior by enhancing localized plasticity. These findings emphasize the interplay between SFE, strain rate, and phase transformation in governing the cryogenic mechanical performance of 304L stainless steel.