Synthesis, Structures, and Transport Properties of Quaternary Ba–Ag–<i>Tr</i>–As Materials (<i>Tr</i> = Ga, In)

The synthesis, structures, and properties of two quaternary barium–arsenide materials are presented. The first, Ba 4 Ag 2.3 In 1.7 As 8 , is a novel material with the monoclinic unit cell ( P 2 1 / m space group). The layered crystal structure of Ba 4 Ag 2.3 In 1.7 As 8 may be considered a lower‐symmetry, distorted analog of the LaCuSb 2 structure. The structure features a rare As fragment, cis‐trans As chains along the [010] direction. Large crystals of Ba 4 Ag 2.3 In 1.7 As 8 can be grown from Bi flux and are used for subsequent transport property measurements. Electrical resistivity and heat capacity properties are reported, establishing Ba 4 Ag 2.3 In 1.7 As 8 as a metallic phase. The second material, Ba 4 AgGa 5 As 8 , is a 3D material that crystallizes in the orthorhombic unit cell (noncentrosymmetric and polar Iba 2 space group). Expanding upon its original discovery, the optimized synthetic profile for single‐phase polycrystalline samples as well as transport properties relevant to thermoelectric applications are presented. Ba 4 AgGa 5 As 8 exhibits a high Seebeck coefficient of 290 μV K −1 at room temperature, indicative of lower carrier concentrations typical for nonmetallic phases. Electrical resistivity measurements also affirm conventional semiconducting behavior for Ba 4 AgGa 5 As 8 .