Effect of molybdenum on high-temperature tribological performance in HVOF sprayed of WC-based coatings on superni-76

This study examines the effects of Mo on the high-temperature wear and friction behavior of HVOF-sprayed 70%WC-Co/25%Mo/5%C and 70%WC-CrC-Ni/30%Mo coatings on Superni-76. The ball-on-disc tribometer wear tests were conducted at different temperatures (300°C and 600°C) and loads (10 and 30 N) against counter body Al 2 O 3 ball. Microstructures and phase formation were investigated using SEM/EDS and XRD. The characterization of coating microhardness, surface roughness, and coating density was examined. The 70%WC-Co/25%Mo/5%C coating showed lower surface roughness and higher microhardness values than the 70%WC-CrC-Ni/30%Mo coating. The wear rate of the substrate increases with an increase in temperature, whereas 70%WC-Co/25%Mo/5%C and 70%WC-CrC-Ni/30%Mo coatings decrease with temperature from 300°C to 600°C. The coefficient of friction of substrate and coating decreases with increasing temperatures. The worn surfaces of 70%WC-Co/25%Mo/5%C and 70%WC-CrC-Ni/30%Mo coating contain oxide phases (WO 3 , Cr 2 O 5 ) and lubrication phases (M 0.2 W 0.8 O 3 , CoMoO 4, and MoO 3 ) at 600°C. These oxide phases reduced the coating wear rate and coefficient of friction at 600°C. The 70%WC-Co/25%Mo/5%C coating showed improved resistance to wear and lower friction coefficient than the substrate and 70%WC-CrC-Ni/30%Mo coating. At temperatures of 300°C, the main abrasive wear mechanism changes to oxidative wear when the temperature reaches 600°C for both coatings.