Properties of Composites from Curauá Fibers and High-Density Bio-Based Polyethylene: The Influence of Processing Methods

The study examined composites composed of curauá fibers (10%) and a high-density bio-based polyethylene (HDBPE) matrix, emphasizing the effects of processing methods on their final properties. In addition, plant-derived oils were applied as compatibilizers to improve the interfacial adhesion between the hydrophilic fibers and the hydrophobic HDBPE, thereby supporting the process’s sustainability. The comparative analysis of HDBPE/curauá fiber/plant-based oil composites utilized distinct methodologies: compounding with an internal mixer, followed by thermopressing and mixture composition using a twin-screw extruder with subsequent injection molding. Castor oil (CO), canola oil (CA), or epoxidized soybean oil (OSE) were employed as compatibilizers (5%). All composites displayed high levels of crystallinity (up to 86%) compared to neat HDBPE (67%), likely due to interactions with curauá fibers and compatibilizers. The use of twin-screw extruder/injection molding produced composites with higher impact and flexural strength/modulus-assessed at 5%(approximately 222 J/m to 290 J/m; 22/700 MPa to 26/880 MPa, respectively), considerably exceeding those formed via internal mixer/thermopressing (approximately 110 J/m to 123 J/m; 14/600 MPa to 20/700 MPa). Micrographs of the composites indicated that the extruder separated the fiber bundles into smaller-diameter units, which may have facilitated the transfer of load from the matrix to the fibers, optimizing the composite’s mechanical performance. As a compatibilizer, CO enhanced both properties and, when combined with the twin-screw extruder/injection technique, emerged as the optimal choice for HDBPE/curauá fiber composites.