Photoluminescence and Thermoluminescence Studies of Beta‐Irradiated Ba <sub>3</sub> CdSi <sub>2</sub> O <sub>8</sub> :Tb <sup>3+</sup> Phosphor for LED and Dosimetry Applications
The present work reports the preparation, characterization, and photoluminescence (PL) and thermoluminescence (TL) responses of Tb<sup>3+</sup>-doped Ba₃CdSi₂O₈ phosphors. X-ray diffraction analysis confirmed the consistency of the Tb<sup>3+</sup>-doped Ba₃CdSi₂O₈ samples with the PDF 00-028-0128 card structure. The TL glow curve of the material was examined at different dopant concentrations after irradiation with a <sup>90</sup>Sr/<sup>90</sup>Y beta source. Among the samples, Ba₃CdSi₂O₈: 5% Tb<sup>3+</sup> exhibited the highest TL intensity compared with the other concentrations. The glow curve deconvolution method was used to determine the number of peaks, trap structure, and kinetic parameters within the TL glow curve, yielding a figure of merit (FOM) value of 1.11. The PL spectra show that the 2.0%, 3.0%, 4.0%, 5.0%, and 6.0% mole Tb<sup>3+</sup>-doped Ba₃Cd (SiO₄)₂ phosphors capture excitation energy through the 4f-5d transitions of Tb<sup>3+</sup> ions and emit light at 417, 440, 492, 552, 589, and 628 nm, corresponding to the 5D₃-7F₅, 5D₃-7F₄, 5D₄-7F₆, 5D₄-7F₅, 5D₄-7F₄, and 5D₄-7F₃ transitions, respectively.
Authors
- V. Emir Kafadar (ORCID: https://orcid.org/0000-0002-0806-0943)
- Fatih Mehmet Emen (ORCID: https://orcid.org/0000-0002-4974-2940)
- Ali İhsan Karaçolak (ORCID: https://orcid.org/0000-0002-6680-3290)
- Esra Öztürk (ORCID: https://orcid.org/0000-0002-4522-6500)
- B. Basaran
Institutions
- Karamanoğlu Mehmetbey University (TR)
- Burdur Mehmet Akif Ersoy Üniversitesi (TR)
- Gaziantep University (TR)
- Hacettepe University (TR)
Publication Details
- Journal
- Luminescence
- Published
- 2025-04-01
- DOI
- https://doi.org/10.1002/bio.70171
- Citations
- 1
- Primary Topic
- Luminescence Properties of Advanced Materials
- Type
- article
- Field-Weighted Citation Impact
- 0.52
Funders
- Gaziantep Üniversitesi