Interfacial Characteristics and Mechanical Performance of IN718/CuSn10 Fabricated by Laser Powder Bed Fusion

To address the critical applications of heterogeneous structures involving nickel-based superalloys (IN718) and copper alloys (CuSn10) under extreme operating conditions, and to address the limitations of traditional joining techniques in terms of interfacial brittleness and geometric constraints, this study employs Laser Powder Bed Fusion (LPBF) technology, specifically multi-material LPBF (MM-LPBF). By precisely melting IN718 and CuSn10 powders layer by layer, the study directly fabricates multi-material IN718/CuSn10 joint specimens, thereby simplifying the complexity of traditional joining processes. The research systematically investigates the interfacial microstructure and mechanical property evolution laws and underlying mechanisms. It reveals that sufficient element diffusion and hardness gradients are present at the IN718/CuSn10 interface, indicating good metallurgical bonding. However, due to significant differences in thermophysical properties, cracks inevitably appear at the interface. Mechanical property tests indicate that the strength of the IN718/CuSn10 joint specimens falls between that of IN718 and CuSn10, but with lower elongation, and fractures primarily occur at the interface. This research provides theoretical support for establishing a process database for LPBF formed of nickel–copper heterogeneous materials, advancing the manufacturing technology of aerospace multi-material components.