Copper Molybdate-Catalyzed Esterification of Levulinic Acid: A Heterogeneous Approach for Biofuel Synthesis

The catalytic esterification of levulinic acid (LA) to methyl levulinate (ML) was investigated using copper molybdate (Cu3(MoO4)2(OH)2) as a heterogeneous catalyst. The catalyst, synthesized via chemical precipitation, exhibited a monoclinic structure with self-assembled nanoplates forming spherical mesostructures. Structural characterization confirmed its high crystallinity, while textural analysis revealed a BET surface area of 70.55 m2 g−1 with pore sizes in the nanometric range (1–6 nm). The catalytic performance was systematically evaluated under varying reaction conditions, including temperature, catalyst dosage, reaction time, methanol-to-LA molar ratio, alcohol type, and catalyst reusability. Optimal conversion of 99.3% was achieved at 100 °C, a 1:20 methanol-to-LA molar ratio, 5% catalyst loading, and a reaction time of 4 h. Comparative analysis with other heterogeneous catalysts demonstrated superior efficiency and stability of Cu3(MoO4)2(OH)2, with minimal activity loss over four reuse cycles (final conversion of 77.1%). Mechanistic insights suggest that its high activity is attributed to Lewis and Brønsted acid sites, facilitating efficient esterification. This study underscores the potential of copper molybdate as a sustainable and recyclable catalyst for biofuel additive synthesis, advancing green chemistry strategies for biomass valorization.