Experimental investigation on the performance of ground granulated blast furnace slag and copper slag blended recycled aggregate concrete exposed to elevated temperatures

The current experimental programme examines the residual performance of recycled aggregate concrete (RAC) under elevated temperatures, with partial replacement of fine aggregate by copper slag , followed by the substitution of cement with ground granulated blast furnace slag (GGBFS). RAC was prepared by replacing natural coarse aggregate with recycled coarse aggregate (RCA) at substitution levels of 0 %, 33 %, 66 %, and 100 %. Among these, the 33 % RCA replacement demonstrated superior mechanical properties and was selected for further investigation. Subsequently, the industrial wastes like copper slag and GGBFS were used for replacing fine aggregate and cement up to 60 % to escalate the residual characteristics of RAC mixes prepared with 33 % RCA. All the specimens were exposed at temperature level of 30 °C, 200 °C, 400 °C, 600 °C and 800 °C respectively and assessed their residual compressive strength , split tensile strength , elastic modulus , and failure behavior by conducting laboratory experiments. Test results concluded that, the GGBFS and CS blended RAC mixture achieved greater resistance to deterioration of strength properties compared to the control mixture at higher temperature. The combination of 33 % RCA, 40 % CS, and 40 % GGBFS exhibited superior residual performance over all the mixes and established grater fire-resistant to concrete. Further, the microstructural study of different RAC mixtures revealed that the addition of CS and GGBFS strengthened the RAC matrix by creating a dense calcium silicate hydrate gel. • Workability of RAC increases with the addition of CS and GGBFS. • RAC with 40 % CS and 40 % GGBFS achieves the highest residual mechanical properties. • Microstructural properties of RAC improved on inclusion of copper slag and GGBFS. • RAC using CS and GGBFS is more environmentally friendly and fire resistant.