Aging Behavior of 10CrNi2Mo3Cu2V Maraging Alloy: Clustering, Precipitation, and Strengthening

The high-temperature performance of 10CrNi2Mo3Cu2V steel is critically governed by the distribution of Cu-rich phases. This study systematically investigated the evolution of solute redistribution, Cu-rich phase precipitation, microstructural transformations, and mechanical properties in 10CrNi2Mo3Cu2V alloy under varying aging temperatures. Advanced characterization techniques, including atom probe tomography (APT) and transmission electron microscopy (TEM), were employed to analyze microstructural features and phase formation in both as-built and heat-treated specimens. The key findings reveal that copper atom segregation initiates at a tempering temperature of 350 °C. Upon increasing the temperature to 450 °C, extensive precipitation of nanoscale copper clusters is observed. Temperatures exceeding 450 °C trigger the formation of ε-Cu phases, which undergo subsequent coarsening. Notably, these copper clusters and Cu-rich precipitates act as dislocation pinning sites, promoting crack nucleation and propagation, thereby markedly degrading the alloy’s impact energy absorption capacity. The critical diameter for Orowan mechanism-governed strengthening by Cu-rich phases is determined to be ~6 nm, while the average diameter of matrix-penetrating Cu-rich particles is approximately 1.46 nm. Quantitative analysis demonstrated that the combined contributions of the Orowan bypass mechanism and particle-cutting mechanism yield a strength enhancement of ~219 MPa, which exhibits excellent agreement with experimentally measured strength increments. These results provide critical insights into the interplay between microstructural evolution and mechanical degradation in precipitation-strengthened steels under thermal exposure.