Location-Specific Microstructures and Properties of Haynes 282 Alloy with Laser-Wire DED Processing

In this work, the location-specific microstructures in terms of grain morphology, texture, γ′ precipitates, carbides, and residual strains were investigated in a series of laser-wire direct energy deposition (LW-DED) Haynes 282 alloys with varied processing parameters. A bimodal grain distribution was found in these as-printed and heat-treated alloys with columnar grains within the layers and fine equiaxed grains at the interlayer regions. Dominant <001> texture along the build direction with more obvious <111> orientation preference exists at the bottom layers, compared to the top layers. The gradient γ′-precipitates size distribution contributes predominantly to the observed gradient hardness distribution in the as-printed samples. The heat-treated 282 exhibit comparable yield strengths to those conventionally-processed counterparts, while the observed small deviation in their yield strengths is attributed to the Hall-Petch effect. This work establishes the correlation between location-specific microstructures and mechanical properties, providing valuable insights into future printing parameters and heat-treatment optimization.