Characterization of Build Parameters and Microstructure in Low Heat Input WAAM of Ni-Based Superalloy Haynes 282

Ni-based superalloy Haynes® 282® is being targeted for various applications in advanced power generation systems for its superior fabricability, weldability, and excellent high temperature creep and corrosion performance. This process optimization study aims to use a low heat-input, high deposition rate, controlled Gas Metal Arc Welding (GMAW) process, Cold Metal Transfer (CMT) by Fronius, attempting to achieve fully dense fabrication and possibly avoid the need for HIP. Twenty-one multilayer blocks (~25x100x40 mm3) were deposited to explore a large set of build parameters variations that focused on varying the travel speed from 14 to 42 inches per minute (ipm) and wire feed speed from 150 to 450 ipm. A strong correlation has been observed between arc energy – controlled primarily by travel and wire feed speed. Initial visual inspection, internal microstructural examination, and computed tomography (CT) have been used to determine the effects of built parameters on evolution of internal porosity and defects. Scanning electron microscopy techniques enabled structural and compositional imaging of heterogeneity and changes in microstructural properties.