Alkaline Zinc Passivation Mechanism is Controlled by Hydroxide Concentration

We studied Zn passivation and oxide growth in Zincate (Zn(OH) 4 2− ) in 4 and 8 M KOH solutions using an electrochemical quartz crystal microbalance (EQCM), building on our initial work at 1 M KOH where passivation was kinetically controlled. A porous passivating oxide spontaneously forms on Zn electrodes when KOH is above 4 M and saturated with zincate. However, passivation does not occur when bulk zincate concentration is decreased, resulting in continual Zn dissolution. EQCM data suggests that the passivation mechanism is strongly affected by pOH. Mass transport and kinetic processes in the 4 M KOH electrolytes couple and govern Zn passivation. At 8 M, KOH concentration shifts passivation to mass transport control. We explain this by the increased solubility of Zn(OH) 3 − with increasing pOH. The variation in the mechanism of passivation implications for how passivation is handled in Zn-alkaline batteries. The importance of controlling the mass transport increases with increased pOH, suggesting that electrode design, additives, and potential flow should be optimized. At lower pOHs, kinetics and mass transport must be balanced to manage passivation effectively. Additionally, the changing nature of the native oxide layer on the surface has implications for the evenness of deposition and dissolution on the Zn electrode.