Zero-Dimensional Organic Amine-Copper Bromide Hybrid Crystal with Highly Efficient Yellow Emission

Recently, Cu(I)-based metal halides have attracted tremendous attention owing to their remarkable photophysical properties. However, most of them can only be excited by near ultraviolet (UV) light at a wavelength (generally less than 350 nm) with a wide bandgap, which undoubtedly limits their application in solid-state lighting due to the low excitation efficiency at about 400 nm in devices. Here, we report a new zero-dimensional organic cuprous bromide of (C13H30N)2Cu5Br7 single crystals, which can be excited by visible light (390–400 nm) and give a bright yellow and broad self-trapped exciton emission band with the photoluminescence quantum yield (PLQY) of 92.3% at room temperature. The experimental and theoretical results show that the existence of Cu-Br-Cu metal bonds in a Cu5Br7 cluster package produces three components of self-trapped excitons (STE) that emit at room temperature but merge into one at 80 K. This occurs because of the anomalously enhanced electron–phonon coupling and electron–electron coupling in the coupled clusters in this system. These effects cause the excitation near visible light and emission broader at higher temperature. Additionally, their remarkable anti-water emission stability was demonstrated even after soaking in water for 6 h. Finally, a highly efficient white-light-emitting diode (WLED) based on (C13H30N)2Cu5Br7 was fabricated.