Influence of Preheating on the Microstructure of a Hot Extruded Nickel-Based Superalloy

Some studies have reported the microstructure evolution of nickel-based superalloys during isothermal forging (IF). However, most of them have not taken into account the microstructure evolution during the preheating stage in manufacturing processes. Investigating the microstructure evolution mechanisms during preheating of nickel-based superalloy can provide a more accurate characterization of the initial microstructures prior to IF. In this study, the evolution of grain structure, participation phase, and twins in a hot extruded nickel-based superalloy are examined during heat treatment at the temperature range of 1050~1140 °C and 5~180 min. Also, the interaction mechanisms among the above microstructures are analyzed. Experimental results demonstrate that higher temperature significantly accelerates the dissolution of the primary γ' (γ'<sub>p</sub>) phase and grain growth. At 180 min, the average grain size rapidly grows from 4.59 μm at 1080 °C to 14.09 μm at 1110 °C. In contrast, the impact of holding time on the microstructure diminishes after 30 min. At 1080 °C, the average grain size grows from 2.52 μm at 5 min to 4.95 μm at 30 min, after which it remains relatively stable. Initially, the γ'<sub>p</sub> phase hinders grain boundary migration and inhibits grain growth. However, its complete dissolution at high temperatures significantly promotes grain growth. Careful selection of preheating temperature can mitigate rapid grain growth before forging. Additionally, twins not only refine grains through nucleation and segmentation, but also hinder grain boundary migration in regions with high dislocation density, thereby alleviating grain growth. A model detailing the dissolution of the γ'<sub>p</sub> phase during preheating is developed, with a correlation coefficient and average absolute relative error of 0.9947 and 9.15%, respectively. This model provides theoretical support for optimizing preheating temperatures and estimating initial microstructures prior to IF.

Authors

Institutions

Publication Details

Journal
Materials
Published
2025-03-26
DOI
https://doi.org/10.3390/ma18071478
Citations
1
Primary Topic
Metallurgy and Material Forming
Type
article
Field-Weighted Citation Impact
0.86

Funders

Controls
|||
ALL TIME
JAN
FEB
MAR
APR
MAY
JUN
JUL
AUG
SEP
OCT
article

Influence of Preheating on the Microstructure of a Hot Extruded Nickel-Based Superalloy

Y.C. Lin, Yu-Liang Qiu, Zijian Chen, Juncheng Zhu et al.
1 citations
Materials
Metallurgy and Material Forming
0.86
article

Influence of Preheating on the Microstructure of a Hot Extruded Nickel-Based Superalloy

Y.C. Lin, Yu-Liang Qiu, Zijian Chen, Juncheng Zhu, Shuxin Li, Yunhan Ling
article en
1 citations

Abstract

Some studies have reported the microstructure evolution of nickel-based superalloys during isothermal forging (IF). However, most of them have not taken into account the microstructure evolution during the preheating stage in manufacturing processes. Investigating the microstructure evolution mechanisms during preheating of nickel-based superalloy can provide a more accurate characterization of the initial microstructures prior to IF. In this study, the evolution of grain structure, participation phase, and twins in a hot extruded nickel-based superalloy are examined during heat treatment at the temperature range of 1050~1140 °C and 5~180 min. Also, the interaction mechanisms among the above microstructures are analyzed. Experimental results demonstrate that higher temperature significantly accelerates the dissolution of the primary γ' (γ'<sub>p</sub>) phase and grain growth. At 180 min, the average grain size rapidly grows from 4.59 μm at 1080 °C to 14.09 μm at 1110 °C. In contrast, the impact of holding time on the microstructure diminishes after 30 min. At 1080 °C, the average grain size grows from 2.52 μm at 5 min to 4.95 μm at 30 min, after which it remains relatively stable. Initially, the γ'<sub>p</sub> phase hinders grain boundary migration and inhibits grain growth. However, its complete dissolution at high temperatures significantly promotes grain growth. Careful selection of preheating temperature can mitigate rapid grain growth before forging. Additionally, twins not only refine grains through nucleation and segmentation, but also hinder grain boundary migration in regions with high dislocation density, thereby alleviating grain growth. A model detailing the dissolution of the γ'<sub>p</sub> phase during preheating is developed, with a correlation coefficient and average absolute relative error of 0.9947 and 9.15%, respectively. This model provides theoretical support for optimizing preheating temperatures and estimating initial microstructures prior to IF.

MaterialsVol. 18(7)
Ningbo University (CN), Central South University (CN), Beijing Research Institute of Mechanical and Electrical Technology (CN), China Academy Of Machinery Science & Technology (China) (CN), Rongcheng City People's Hospital (CN)
Hunan Provincial Innovation Foundation for Postgraduate, National Key Research and Development Program of China
Openalex Percentile: Top 33%
Metallurgy and Material Forming
0.86
AI Navigator

Ask Laika to Summarize, Analyze, and Connect papers live on the map.

Summarize Papers & Methodologies

Extract key findings, datasets, and comparative methods across publications.

Benchmark Rankings & Visual Analytics

Rank top research institutions, authors, funders, topics, and journals by Field-Weighted Citation Impact (FWCI) and paper volume with instant charts.

Connect Distant Disciplines

Bridge topological clusters on the map to find hidden collaborative intersections.