Tribology of self-mated siliconized graphite under high pv factors in high-temperature and high-pressure water

To enhance the structural design reliability, certain operating conditions for the combination of high contact pressure and sliding velocity are desired in an advanced main coolant pump. The tribological properties of self-mated 22C-64SiC-14Si (vol%) siliconized graphite are investigated using a high-temperature and high-pressure water-lubricated tribometer on pin-on-disc configuration under high pv factors of 0.4–68.8 MPa·m/s at applied loads p of 500 and 1200 N with spindle speeds v of 100–6000 rpm in 50 °C and 1.5 MPa water environment. With the pv factor from 1.1 to 68.8 MPa·m/s, the wear depth decreases from 0.98 μm to 0.12 μm, the average COF declines from 0.030 to 0.010, and a smooth worn surface is noted, despite a slight increase in surface roughness Ra from 0.015 to 0.023 μm. An oxidation layer is observed on the SiC of siliconized graphite by scanning electron microscope (SEM) and transmission electron microscopy (TEM) with energy dispersive spectroscopy (EDS) analysis. The abrasive wear of the SiC and Si asperities, in conjunction with the solid lubrication provided by graphite, is ascribed to boundary lubrication influenced by the high pv factor. The tribochemical wear under hydrodynamic lubrication occurs between the SiO 2 layers on the SiC surface. The wear mechanism in mixed lubrication is contingent upon the contact ratio determined by the pv factor. In order to achieve the hydrodynamic lubrication regime of the siliconized graphite under high pv factor, it is necessary either to increase the sliding speed or to reduce the contact stress. • High pv for self-mated siliconized graphite pairs in high-temperature and high-pressure water. • A low COF and wear depth of siliconized graphite pairs under 1.1–68.8 MPa·m/s. • An oxidation layer is observed on the SiC of siliconized graphite by SEM and TEM with EDS. • Abrasive of SiC and Si asperities in boundary lubrication and tribochemical wear in hydrodynamic. • Wear mechanism in mixed lubrication is contingent upon the contact ratio determined by pv .