Enhanced Stability and Adsorption of Cross-Linked Magnetite Hydrogel Beads via Silica Impregnation

Hydrogel-based adsorbents have gained increasing recognition in recent years due to their promising potential for pollutant removal. However, conventional hydrogels often suffer from low mechanical strength over prolonged use. Therefore, this study explores the incorporation of silica extracted from bamboo culm (Dendrocalamus asper) to enhance the mechanical stability of hydrogel beads composed from carboxymethyl cellulose (CMC), chitosan (CS), and magnetite ferrofluid (Fe3O4), through cross-linking. We hypothesize that silica enhances the mechanical properties of magnetite hydrogel beads without compromising their adsorption capacity. The extracted silica was confirmed with FTIR and EDS analysis. The synthesized CMC-CS-Fe3O4-Si hydrogel beads were characterized using FTIR and SEM. Its stability was assessed through dry weight loss measurements, while its adsorption efficiency was evaluated using batch adsorption experiments. The silica-incorporated hydrogel exhibited enhanced mechanical and thermal stability under various pH and temperature conditions, without negatively affecting its adsorption performance, achieving maximum adsorption capacities of 53.00 mg/g for Cr (VI) and 85.06 mg/g for Cu (II). Desorption and regeneration studies confirmed the reusability of the hydrogel for more than four cycles. Overall, the interaction between the hydrogel and silica resulted in excellent adsorption performance, improved mechanical properties, and long-term reusability, making this a promising hydrogel adsorbent for wastewater remediation.