Effect of Al-3Ti-4.35La Master Alloy on the Aggregation and Sedimentation Characteristics of TiC in Al-7Si Alloys

The Al-Ti-C alloy is the most widely used grain refiner for Al-7Si alloys. However, TiC particles in Al-7Si alloys tend to aggregate and settle, thereby reducing their refinement efficiency. In the present paper, a novel Al-3Ti-4.35La master alloy was developed, and its influence on the stability of TiC particles in Al-7Si alloys was investigated by XRD, SEM, and TEM. The results show that when the Al-TiC alloy is added to the Al-7Si alloy, TiC will accumulate and settle obviously after holding the alloy for a certain time (15 min, 30 min, and 60 min). When the Al-TiC alloy and the Al-3Ti-4.35La master alloy are added to the Al-7Si alloy, the aggregation and settlement of TiC are weakened under the same holding time. Additionally, the refinement effect of TiC is enhanced. The Ti and La elements dissolved by Ti2Al20La in the Al-3Ti-4.35La master alloy are absorbed on the surface of the TiC particles, which improves the wettability between the TiC particles and the aluminum melt, reduces the agglomeration and sedimentation of TiC particles in the aluminum melt, and improves its stability.