Chemical Synthesis of Nanostructured Topological Pb1−xSnxSe (x = 0–1) Alloy Films—A Study of Their Structural, Optical, and Thermopower Properties

The spray pyrolysis deposition of nanostructured Pb1−xSnxSe alloy films, x = 0.0 to 1.0, from as-prepared Pb1−xSnxSe alloy colloids as the starting solution is reported. The colloidal dispersions were prepared by dissolving selenium in an amine–thiol mixture, reacted with the Sn and Pb precursors in propylene glycol, and subsequently sprayed onto glass substrates at 300 °C. Structural characterization indicated the formation of the alloyed rock-salt cubic phase for 0.0 ≤ x ≤ 0.75, oxidized Pb and Se phases produced during the deposition, and only orthorhombic SnSe for x = 1.0 with Se and SnSe2 as impurities. Nanocrystalline films ranging from 16 to 16.5 nm in size were obtained. The films displayed a shift in their optical structure and a non-monotonic variation in the band gap energy, first a decrease, reaching the minimum at x = 0.30 and a further increase in the Sn content. The decrease in the optical band gap resembles that of a topological insulator behavior. The morphology of the alloyed films confirmed the large nanocrystal formation by self-assembly processes in both the PbSe and SnSe phases and segregated PbSnSe platelets for x ≥ 0.30. Seebeck coefficient revealed that a typical semiconductor behavior dominated by bipolar transport, and p-type conductivity, but only for x = 0.0 n-type conductivity was exhibited. The maximal Seebeck coefficient magnitude behaved similarly to the band gap energy, evidencing the influence of energy band structure and the topological character.