Effect of Superheated Steam Technology on the Deformation Recovery Performance of Teakwood Bending Components and Its Mechanism

To address the issue of the deformation recovery in teakwood bending components when they undergo moisture absorption, the potential for superheated steam technology to improve the dimensional stability of the material and the means of optimizing this improvement were systematically analyzed. After setting a medium temperature, treatment time, and initial moisture content, we performed a 120 h water immersion test and dynamic thermo-mechanical analysis (DMA), which revealed the multi-scale mechanism by which superheated steam technology inhibits deformation recovery. It was shown that under the optimized conditions of 130 °C, a 2 h treatment time, and a 30% initial moisture content, the deformation recovery of water-immersed teakwood bending components could be reduced to 2.02–5.13%. The water-absorption resilience was decreased by 41.05% compared with the conventional drying and shaping, which was attributed to the synergistic effect of the degradation of hemicellulose and the cross-linking of lignin, which released residual stresses efficiently. Our investigation of the chemical–mechanical coupling revealed a significant positive correlation between the water-absorption resilience and the hemicellulose content (R2 = 0.912), and the interaction of the chemical constituents resulted in a directional evolution of the energy storage modulus and loss modulus, which enhanced the stiffness of the material and effectively inhibited water-absorption resilience. This study provides a theoretical basis and process guidance for the efficient industrialization of solid wood bending components, which has important guiding value for the innovation of manufacturing technology for bending wood furniture.