Construction of High-Load-Bearing Capacity Polyamide-Imide Self-Lubricating Coatings with Various Nanoparticles Through Worn Surface of Cobblestone-like Road

Polymer composite coatings exhibit excellent mechanical properties, chemical resistance, and self-lubricating characteristics, providing an effective solution to address the failure of transmission components under harsh operating conditions, including high-speed, high-pressure, and oil-deficient environments, which often lead to excessive friction and limited bearing performance. This study fabricated three polyamide-imide (PAI) composite coatings modified with monodisperse surface-modified nano-silica (SiO2) via direct spraying and compared their physicochemical parameters. The tribological performance of the three coatings was evaluated using ring-block high-speed friction and wear tester under continuous loading conditions. The tests were conducted using diesel engine oil CI4-5W40, supplemented with oil-soluble cerium dioxide (CeO2) nanoparticles as an energy-efficient and restorative additive, as the lubricating medium. The experimental results demonstrated that the PAI composite coating exhibited a load-bearing capacity exceeding 1000 N (66 MPa). The wear mechanism analysis reveals that CeO2 nanoparticles embedded in the coating surface form a cobblestone-like protective layer. This unique microstructure compensates for the surface pits generated by PAI matrix transfer and minimizes direct contact between the coating and steel ring. Additionally, the synergistic interaction between short carbon fiber (SCF) and the tribofilm contributes to the exceptional tribological properties of the coating, including coefficients of friction as low as 0.04 and wear rates below 0.41 × 10−8 mm3/N·m. The experimental findings could provide an experimental and theoretical foundation for the application of coatings under conditions involving finished lubricants.