Preparation and performance of ZSM-5/MoS₂/PTFE coating for enhancing wear and corrosion resistance

The wear and corrosion resistance of water-based polytetrafluoroethylene (PTFE) coating need to be further improved to cope with various harsh environmental conditions. In this paper, a mulberry-like ZSM-5 molecular sieve was prepared and then was modified to enhance the uniformity, wear resistance and hardness of PTFE coating. In addition, a ZSM-5/MoS₂/PTFE coating was developed by adding MoS₂in the chemical composition of coatings, which significantly increased the critical cracking thickness of PTFE to 27<i>μ</i>m. The wear amount of ZSM-5/MoS₂/PTFE coating is only 5.7 mg, and after 680 h of salt spray, there is no obvious corrosion on the surface. The friction coefficients under applied loads of 5 N, 10 N, and 20 N are 0.007, 0.057, and 0.055, respectively. The experiment results show that the coating possesses excellent lubrication, wear resistance, and corrosion resistance, and its performance and cost are far superior to commercial products.