Achieving High Strength and Plasticity by Controlling the Volume Fractions of Martensite and Ferrite in Rare Earth, Micro-Alloyed Dual-Phase Steel

The volume fractions of martensite and ferrite in dual-phase steel affect its strength and plasticity. In this study, the effect of heat treatment on the structure morphology and volume fractions of martensitic and ferrite was studied in rare earth, micro-alloyed dual-phase steel, and the strain-hardening behaviour of the experimental steel under various process conditions was determined. The results show that a uniform structure with an alternating distribution of ferrite and martensite could be obtained by complete quenching before critical annealing, and the martensitic phase content increased from 60% to 93% with a rise in annealing temperature. With the growth in the martensitic phase content, the strength of dual-phase (DP) steel gradually increased, and elongation gradually decreased. However, the strength–plasticity product remained at approximately 17 GPa∙%, showing good comprehensive mechanical properties, and the mechanical properties were better at 780 and 820 °C annealing temperatures. When the martensite content was higher, the strain-hardening ability of the DP steel was stronger. The results show that the failure mode of the DP steel was a typical ductile fracture, and only a small amount of cleavage pattern was observed in the samples annealed at 840 °C. No obvious interfacial disbonding was seen in the tensile fracture, and only a few cracks formed. By optimizing the heat treatment process, the microstructural uniformity was improved, and the ferrite phase was strengthened to some extent, which better coordinated the deformation of ferrite and martensite, thereby delaying fracture. The modification effect of rare earth elements on inclusions in the DP steel was obvious.