Utilization of lime-mixed geopolymerized rice husk ash (LGR) for balanced amelioration of collapsible soil

Structures constructed on collapsible soil are prone to failure under flooding. Agro-waste like rice husk ash (RHA) and its geopolymer (LGR), consisting of lime (L), RHA, water glass (Na 2 SiO 3 ), and caustic soda (NaOH), present a potential solution to address this issue. RHA and LGR were mixed up to 16% to improve the collapsible soil. Samples were remolded at optimal water content and maximum dry density for strength and collapsible potential tests. Unconfined compressive strength, deformation modulus, and soaked California bearing ratio exhibit exponential improvement with the inclusion of LGR. Additionally, for comparison of microstructural characteristics, analyses involving energy-dispersive X-ray spectroscopy (EDAX) and scanning electron microscope (SEM) were conducted on both virgin and treated specimens. LGR resulted in the emergence of new peaks of sodium silicates and calcium silicates, as indicated by EDAX. The formation of H-C-A-S gel and H-N-A-S gel observed in SEM suggests the development of bonds among soil particles attributed to geopolymerization. SEM reveals the transformation of the inherent collapsible soil from a dispersed and silt-dominated structure to a reticulated structure devoid of micro-pores following the incorporation of LGR. A numerical model was constructed to forecast the performance of both virgin and stabilized collapsible soils under pre- and post-flooding conditions. The outcomes indicate an enhancement in the soil's bearing capacity upon stabilization with 12% LGR. The implementation of 12% LGR significantly resulted in a lower embodied energy-to-strength ratio, emissions-to-strength ratio, and relatively lower cost-to-strength ratio compared to the soil treated with 16% cement kiln dust (CKD).