Investigation of the Mechanical and Magnetic Property Changes in Austenitic Stainless Steel AISI 304 After Cold Rolling Under Various Heat Treatment Conditions

This study systematically investigates the influence of heat treatment on the mechanical and magnetic properties of AISI 304 austenitic stainless steel following cold rolling. Experimental analyses were conducted on samples annealed at 50 °C to 1200 °C in 25 °C increments. The mechanical properties were characterized through chemical and metallographic analyses, microhardness testing, hardness measurements, and tear-off force evaluations. Magnetic properties were assessed using a fluxgate sensor to analyze the intrinsic magnetic field variations. The findings reveal that the magnetic field intensity peaks at an annealing temperature of 100 °C, followed by a progressive decline up to 700 °C. A pronounced reduction in magnetic properties was observed at 500 °C, with stabilization beyond 700 °C. Notably, the increase in magnetic field intensity at 100 °C suggests a potential transformation of deformation-induced martensite back into austenite. These results provide insights into the thermal stability of cold-rolled AISI 304 stainless steel and its structural evolution, contributing to a deeper understanding of its mechanical and magnetic behavior under varying heat treatment conditions.